Product Details:
Payment & Shipping Terms:
|
Type1: | Ceramic Honeycomb Preheating Furnace | Material: | Ceramic Honeycomb |
---|---|---|---|
Type 2: | Melting Furnace | Type 3: | Cordierite Honeycomb |
Type 4: | Ceramic Honeycomb | Type 5: | Regenerative Burner |
High Light: | basic refractory bricks,stove fire bricks |
furnace refractory bricks Cordierite Ceramic Plate honeycomb for infrared catalytic gas burner
It is applied for accumulated and releasing the heat in the regenerative type burner.
Regenerative Thermal/Catalytic Oxidizer (RTO/RCO) are used to destroy Hazardous Air Pollutants (HAPs), Volatile Organic Compounds (VOCs) and odorous emissions etc, which are extensively applied in the fields of Automotive paint, Chemical industry, Electronic & Electric Manufacturing industry, Contact Combustion System, and so on. Ceramic Honeycomb is specified as structured regenerative media of RTO/RCO.
Advantage
1. Variety of materials & specifications
2. Big specific surface area
3. Small resistance loss
4. Low thermal expansion coefficient
5. High water absorb rate
6. Outstanding crack-resistance
Chemical & Physical Analysis
Chemical & Physical index | Cordierite | Dense Cordierite | Cordierite- mullite | Mullite | Corundum-mullite | |
Chemical Composition (%) | SiO2 | 45~55 | 45~55 | 35~45 | 25~38 | 20~32 |
AI2O3 | 30~38 | 33~43 | 40~50 | 50~65 | 65~73 | |
MgO | 10~15 | 5~13 | 3~13 | - | - | |
K2O+Na2O | <1.0 | <1.0 | <1.0 | <1.0 | <1.0 | |
Fe2O3 | <1.5 | <1.5 | <1.5 | <1.5 | <1.5 | |
Thermal Expansion Coefficient 10-6/K-1 | <2 | <4 | <4 | <5 | <7 | |
Specific Heat J/kg·K | 830~900 | 850~950 | 850~1000 | 900~1050 | 900~1100 | |
Working Temperature ℃ | <1300 | <1300 | <1350 | <1450 | <1500 | |
PS: we also can make products at your request and actual operating condition. |
Product Specifications
Size(mm) | Hole Qty(N×N) | Hole density(cpsi) | Hole Diameter(mm) | Wall thickness(mm) | Porosity (%) |
150×150×300 | 5×5 | 0.7 | 27 | 2.4 | 81 |
150×150×300 | 13×13 | 4.8 | 9.9 | 1.5 | 74 |
150×150×300 | 20×20 | 11 | 6.0 | 1.4 | 64 |
150×150×300 | 25×25 | 18 | 4.9 | 1.00 | 67 |
150×150×300 | 40×40 | 46 | 3.0 | 0.73 | 64 |
150×150×300 | 43×43 | 53 | 2.79 | 0.67 | 64 |
150×150×300 | 50×50 | 72 | 2.4 | 0.60 | 61 |
150×150×300 | 59×59 | 100 | 2.1 | 0.43 | 68 |
Categories
|
Name | Cordierite |
Mullite
|
Corundum mullite |
Chromium oxide
|
Chemical composition
|
Aluminum oxide Al2O3 |
32-40 | 64-68 | 69-74 | 55-60 |
SiO2 | 42-48 | 25-30 | 18-25 | 27-32 | |
MgO | 5-18 | ≤3.0 | ≤3.0 | <1.5 | |
Fe2O3 | ≤1.0 | ≤1.0 | ≤1.0 | <1 | |
Physical properties
|
Density (g/cm3) | >2.2 | 2.2-2.4 | >2.6 | 2.6-3.2 |
Coefficient of thermal expansion (20-1000℃)10-6.K-1 |
2.0-3.5 | 5.0-6.5 | 4-7 | 4-7 | |
Heat capacity (J/kgk) |
800-1200 | 1100-1300 | 800-1000 | 1000-1500 | |
Heat shock (k) | 250min | 230min | 150min | 120min | |
The maximum operation temperature (℃) | 1400 | 1500 | 1600 | 1650 | |
Refractoriness(℃) | 1500> | 1790> | 1800> | 1800> |
Contact Person: sales